Two views of a twinned lost wax cast copper alloy figurine from Ngre Kataa, Mound 6, Unit 44N 6W, Feature 5 cluster. Height: 5.9 cm. Weight: 31.3 g. Ngre Kataa, 19 July, 2008.
Miniature lost wax cast spoon, perhaps a gold weight. From Ngre Kataa, Mound 7, Unit 14N 22E, Level 8. Length: 4.3 cm. Weight: 2.1 g. Ngre Kataa, 27 June, 2009.
Finger ring made from twisted copper alloy wire. From Ngre Kataa, Mound 6, Unit 44N 4W, Level 5. Width: 2.3 cm. Weight: 1.6 g. Ngre Kataa, 8 July, 2009.
A twinned lost wax cast copper alloy figurine from Ngre Kataa, Mound 6, Unit 44N 6W, Feature 5 cluster. Archaeologists interpret the Feature 5 cluster as a shrine placed among metalworking facilities. Height: 5.9 cm. Weight: 31.3 g. Ngre Kataa, 19 July, 2008.
A perforated pottery jar lidded with the pedestaled base of another pot sits in situ at the base of level 6, unit 46N 2W at Mound 6. The pot contained eight cowries and is interpreted by archaeologists as a shrine pot placed in association with metalworking facilities. Photo scale in 5 cm increments. Site Ngre Kataa. 24 June, 2009.
Photo of a partial rim and neck of a mica- and red-slipped everted jar, with vessel profile depicted, left. Red slip has been applied to the rim. Overall mica slip covers the area from the neck down. The neck area is decorated with closely spaced horizontal grooves, with mica slip applied over top. A row of dentate (comb) impression marks the transition to a mica-slipped, but otherwise undecorated, body. INAA sample ("Banda 40-11") assigned to the "L" group of ceramic fabrics; therefore, likely made from clays mined west of the Banda hills. Rim diameter 24 cm at exterior lip. Neck diameter 16 cm at interior constriction. Scale in cm. Ngre Kataa (Banda 40), 30 March, 2001.
Rights:
Creative Commons Attribution--NonCommercial
Publisher:
University of Victoria Libraries
Provenance:
Ngre Kataa, Mound 4, Unit 1, Level 27
Date:
2001-03-30
Location(s) Facet:
Ngre Kataa
Subjects:
Mica slip; Red slip; Dentate impression; Jar; Neutron Activation Analysis
Side view of a broken pottery sherd with a large slag inclusion. The use of crushed slag as a tempering material included in potting clay is first seen in pottery associated with Ngre phase sites in the Banda area. The use of crushed slag as a temper intensifies during Kuulo phase times, after which it becomes uncommon. Ngre Kataa, June, 2008.
Photo of an everted-rim jar excavated from Ngre Kataa, Mound 1, Unit 1, levels 3-6. The jar (Vessel 1) was found upside-down, resting on its rim and in association with a cluster of several other complete (Vessels 2 & 3) and broken pots in what has been interpreted as a kitchen area. The round-based jar is decorated on its lower surface by faint twisted cord-roulette impressions. The zone of cord rouletting is separated from the undecorated surface above by three arching grooves or channels. Multiple small circular punctates mark the place where grooved lines meet. Whole pot. Rim diameter c. 30 cm at exterior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 5 April, 2001.
Iron slag is formed as a byproduct of iron smelting. Here a large slag nodule has broken in half, revealing its interior texture. At the archaeological site of Ngre Kataa, large chunks of 'bubbly' slag like this were occasionally found in household and other contexts, away from areas otherwise associated with metal-working activities. Potters at the time of the site's occupation had begun to use crushed iron slag as a tempering agent in their potting clays, which may explain why large nodules were being carried and cached in areas away from metal-working locations. Ngre Kataa, June, 2008.
Iron slag is formed as a byproduct of iron smelting. Here a large slag nodule has broken in half, revealing its interior texture. At the archaeological site of Ngre Kataa, large chunks of 'bubbly' slag like this were occasionally found in household and other contexts, away from areas otherwise associated with metal-working activities. Potters at the time of the site's occupation had begun to use crushed iron slag as a tempering agent in their potting clays, which may explain why large nodules were being carried and cached in areas away from metal-working locations. Ngre Kataa, June, 2008.
Photo of an everted-rim pottery jar excavated from Ngre Kataa, Mound 4, Unit 1, Levels 5-6. The jar (Vessel 1) was located in the north profile wall of the unit, together with another vessel (Vessel 2).
The jar has a carinated shoulder and a rounded base. To the right and below the carination, a portion of the exterior surface has broken away. The upper area of the jar is decorated with three horizontal grooved lines, inbetween which are lines of dentate impression. Just above the carination is another line of dentate impression and a grooved line. To the left and right, on the upper side of the carination, sets of two triangular designs were applied, consisting of three punctates connected by two short grooved lines. The area inside the triangle is marked by crossed dentate impressions, forming an "X" inside the triangle. This design was repeated twice on the recovered portion of the jar. It was likely repeated a third time on the missing portion. Below the carination are two shallow horizontal grooves. The jar's base is smooth, with no surface treatment applied. Roughly 65% of the vessel was recovered. Rim diameter 25 cm at exterior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 5 April, 2001.
Photo of an everted-rim pottery jar excavated from Ngre Kataa, Mound 4, Unit 1, Level 5. The jar (Vessel 2) was located in the north profile wall of the unit together with another vessel (Vessel 1). The jar has a carinated shoulder and a rounded base. The upper area of the jar is decorated with three horizontal grooved lines inbetween which are lines of dentate impression. The base of the jar is surface treated with a twisted cord roulette. Two roughly parallel horizontal grooved lines separate the cord rouletted zone from a plain zone below the carination. A hole in the base of the pot (ca. 7 cm across) may have been deliberately broken in this otherwise whole pot. Rim diameter 22 cm at exterior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 5 April, 2001.
An iron artifact (SF 09-031) recovered from screened soil taken from the southern end of excavation unit 50N 2W where two large boulders used as anvil/grinding stones were located. In the unit's northwest corner was a burned feature interpreted as the remains of a forge in an area where metalworking took place. The flat iron object is pointed on one end and has two rounded lobes at the other, perhaps to facilitate turning (like a key?). Its function is unknown. The object has been corroded by rusting. Scale in cm. Length: 5.7 cm. Weight: 9.3 g. Site Ngre Kataa. 30 May 2009.
Excavation of a shrine cluster, two images. The image on left shows a pottery cluster, first exposed in June 2008, as it appeared on 10 June 2009. At bottom center of this image is a pedestal base, above which is a tight cluster of rim sherds. The curved sherd on the far right in this image is the outer edge of the pedestal-handled lid, which is fully exposed in the photo on the right, taken on 16 June 2009. A dog skull in a highly friable state is visible above and to the right of this lid in both photos. In the imgae on the right, an iron bangle (SF 09-219) can be seen resting in an angled position, below and left of which is a dog mandible. These were uncovered by excavation below and behind the pedestal base seen in the picture on the left. Photo scale marked in 5 cm increments. Site Ngre Kataa. 10 and 16 June 2009.
An insitu iron bangle (SF 09-132) made from a flattened iron rod with overlapping ends. The bangle occurred as an isolated find in the upper levels of an area (mound 6) that archaeologists interpret as a metallurgical workshop. Photo scales marked in 5 cm increments. Arrow pointing north. Site Ngre Kataa. 6 June 2009.
An iron bangle (SF 09-132) made from a flattened iron rod with overlapping ends. One end of the bangle is bent inward. The bangle occurred as an isolated find in the upper levels of an area (mound 6) that archaeologists interpret as a metallurgical workshop. The bangle has been corroded by rusting. Scale in cm. Width: 7.9 cm. Weight: 25.6 g. Site Ngre Kataa. 6 June 2009.
Photo of an everted-rim pottery jar excavated from Ngre Kataa, Mound 4, Unit 1, Level 20. The jar was located in the west profile wall of the unit. The jar has a carinated shoulder and a rounded base. A single horizontal line of wavy line impression was applied to the neck constriction, with the area above the carination otherwise plain. The base of the jar is surface treated with a fiber (perhaps braided strip) roulette. Two roughly parallel horizontal grooved lines are superimposed over the roulette treatment. Whole pot. Rim diameter 17.5 cm at exterior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 3 April, 2001.
Rights:
Creative Commons Attribution-NonCommercial
Publisher:
University of Victoria Libraries
Provenance:
Ngre Kataa (Banda 40), Mound 4, Unit 1, Level 20, W Wall.
Photo of an everted-rim pottery jar excavated from Ngre Kataa, Mound 4, Unit 1, levels 15-16, where the jar was exposed in the south wall of the excavation unit. The jar has a carinated shoulder and a rounded base. The area above the carination was decorated by five unevenly placed horizontal grooved lines. In three places around the vessel's circumference, the grooved line just above the carination is marked by "ꓥ." In a zone that begins c. 2 cm below the carination, lower areas of the jar are surface treated with a carved roulette impression. The ceramic fabric includes mixed grit (including laterite and quartz) and likely also finely crushed slag. An INAA sample (Banda 40/3) from the jar could not be assigned to a known source group. Roughly 2/3 of the vessel present. Rim diameter: 22.5 cm at interior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 5 April, 2001.
Photo of an everted-rim pottery jar excavated from Ngre Kataa, Mound 4, Unit 1, levels 15-16, where the jar was exposed in the south wall of the excavation unit. The jar has a carinated shoulder and a rounded base. The area above the carination was decorated by five unevenly placed horizontal grooved lines. In three places around the vessel's circumference, the grooved line just above the carination is marked by "ꓥ." In a zone that begins c. 2 cm below the carination, lower areas of the jar are surface treated with a carved roulette impression. The ceramic fabric includes mixed grit (including laterite and quartz) and likely also fine crushed slag. An INAA sample (Banda 40/3) from the jar could not be assigned to a known group. Roughly 2/3 of the vessel present. Rim diameter: 22.5 cm at interior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 5 April, 2001.
Rights:
Creative Commons Attribution-NonCommercial
Publisher:
University of Victoria Libraries
Provenance:
Ngre Kataa (Banda 40), Mound 4, Unit 1, Level 15, South Wall
Photo of an everted-rim jar excavated from Ngre Kataa, Mound 1, Unit 1, Levels 4-5. The jar (Vessel 3) was found sitting upright in association with a cluster of several other complete and broken pots (Vessels 1 & 2) in what has been interpreted as a kitchen area. Most of the jar has been surface treated with a twisted cord roulette. Single pendant grooved lines surround the circumference of the jar. A total of five circular impressions, perhaps made with a hollow reed, are placed below the intersection points of the pendant grooves. A hole in the base of the pot (ca. 7 cm across) may have been deliberately broken in this otherwise whole pot. Rim diameter: 17.5 cm at exterior lip. Site Ngre Kataa ("Banda 40"). 3 April, 2001.
Photo of an everted-rim jar excavated from Ngre Kataa, Mound 1, Unit 1, Levels 4-6. The jar (Vessel 2) was found sitting upright in association with a cluster of several other complete (Vessels 1 & 3) and broken pots in what has been interpreted as a kitchen area. The upper surface of the round-based jar is undecorated. In a zone bounded by double grooved lines, the base and lower surface of the jar is surface treated with maize cob roulette. Groups of three circular punctates mark the spots where gooved lines meet. A hole in the base of the pot (4 x 3.5 cm) may have been deliberately broken in this otherwise whole pot. Rim diameter: 20.5 cm at exterior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 4 March, 2001.
Photo of an everted-rim jar excavated from Ngre Kataa, Mound 4, Unit 1, Level 16. The undecorated exterior surface of the round-based jar is orange-brown from firing, with areas of black fire-clouding. Roughly 30% of jar is represented. Rim diameter: 21 cm at exterior lip. Photo scale in cm. Site Ngre Kataa ("Banda 40"). 28 March, 2001.
A short-stemmed, locally made clay smoking pipe, 2 views (bottom: view from side with pipe bowl to the left; top: view from top). Pipes like this were inspired by those used by America's First Peoples from whom Europeans learned about tobacco. Europeans introduced tobacco smoking to West Africa during the early centuries of trans-Atlantic trade. This pipe's bowl has a flared pedestal base, the bottom of which shows signs of abrasion. Above its base, the pipe bowl is decorated with a zone of criss-cross incisions demarcated by two horizonal incisions (one above and one below). The bowl's rim is missing. Its stem joins the bowl above its base (a "double-angled" form). The stem flares somewhat toward its lip which is flattened. Photo scale in cm. Site Ngre Kataa. 27 May, 2009.
A curved, tanged iron blade (brɔfiɛn in Nafaanra), slightly shouldered at the base (right), with a short narrow tang for the purpose of hafting to a wood handle. The tool shows signs of corrosion. The artfiact was excavated from a house mound. Scale in cm. Length: 19.1 cm. Weight: 54.7 g. Ngre Kataa, 4 June, 2009.
Miniature iron shackles (manacles). The artifact was excavated from a context that archaeologists interpret as a shrine located in metallurgical workshop. The shrine included many pottery jars and lids, iron bangles and other objects. The miniature shackles were placed inside a pottery jar, which was found lying on its side and broken. The shackles have been corroded by rust. Scale in cm. Width: 7.4 cm. Weight: 16.1 g. Site Ngre Kataa. 9-10 June, 2009.
Iron projectile point, the head of which (left) has a rounded base. Two small barbs project from the point's long tang. To make an arrow (snini in Nafaanra), the tang was inserted into a straight shaft made of bamboo, reed or lightweight wood to which it was hafted. This artifact was found in an area that archaeologists interpret as a metallurgical workshop, in the vicintiy of anvil and grinding stones and features interpreted as forges. The projectile point shows signs of corrosion by rusting. Scale in cm. Length: 15.2 cm. Weight: 16 g. Site Ngre Kataa. 4 June, 2009.
Rights:
Creative Commons Attribution-NonCommercial
Publisher:
University of Victoria Libraries
Provenance:
Ngre Kataa, Mound 6, Unit 50N 6W, Level 5. Piece plot 68-79 cm S, 22-23 cm W, 110 cmbd
Triangular-headed iron projectile point with squared base (left) and long tang (right). To make an arrow (snini in Nafaanra), the tang was inserted into a straight shaft made of bamboo, reed or lightweight wood to which it was hafted. This artifact was excavated from what archaeologists interpret as a house mound. It shows signs of corrosion by rust. Scale in cm. Length: 9.6 cm. Weight: 12.6 g. Site Ngre Kataa. 3 June, 2009.
Rights:
Creative Commons Attribution-NonCommercial
Publisher:
University of Victoria Libraries
Provenance:
Ngre Kataa, Mound 7, Unit 10N 30E, Level 6. Piece plot, 44 cm S, 127 cm W, 76 cmbd
Iron projectile point. The head (left) is asymmetrical, perhaps the result of its base being broken. The intact side of the base is shouldered. Two small barbs protrude from opposite sides of the point's long tang (right). To make an arrow, the tang would have been inserted into a shaft made of bamboo, reed or lightweight wood. This point was found in an area (mound 6) that archaeologists interpret as a metallurgical workshop. The artifact has been corroded by rusting. Scale in cm. Length: 10.1 cm. Weight: 8.9 g. Site Ngre Kataa. 4 June, 2009.
A tri-looped iron bangle (SF 09-158) and a flat iron disc (SF 09-159) exposed insitu between two stones. The surfaces of the stones showed signs of use for grinding. This group of objects (cluster D) was found near--and may have been part of--a larger cluster of objects (A-D) that archaeologists interpret as a shrine placed over stratified deposits in a metallurgical workshop. Photo scale marked in 5 cm intervals. Arrow pointing north. Site Ngre Kataa. 9 June 2009.
Asymmetrical barbed iron projectile point with a bent shaft. This artifact was found in an area that archaeologists interpret as a metallurgical workshop. It was found near--and may have been part of--a large cluster of objects interpreted as a shrine. The (partial?) point has been corroded by rusting. Scale in cm. Length: 9.1 cm. Weight: 11.3 g. Site Ngre Kataa, 6 July 2009.
Rights:
Creative Commons Attribution-NonCommercial
Publisher:
University of Victoria Libraries
Provenance:
Ngre Kataa, Mound 6, Unit 48N 8W, Level 6. Piece plot, 5 cm S, 5 cm W, 102 cm bd
Tanged iron blade with pointed tip (left) and rounded shoulders. Two large concretions adhere to the blade's corroded surface. The tang (right) would have allowed the blade to be hafted to a wooden or bamboo shaft or handle. If hafted to a long shaft, it may have been used as a spear (chombo in Nafaanra). This artifact was found closely associated with a copper alloy twinned figurine, an iron bangle, a rounded quartz pebble and several other objects, which archaeologists interpret as a shrine cluster. The cluster was placed among metal-working features in a metallurgical workshop. Scale in cm. Length: 8.6 cm. Weight: 12.6 g. Site Ngre Kataa. 19 July 2008.
A circular iron bangle, made from a rounded iron rod with abutting ends (bottom of photo). The bangle's surface is corroded by rust. This artifact was found closely associated with a copper alloy twinned figurine, a tanged iron blade, a rounded quartz pebble and several other objects, which archaeologists interpret as a shrine cluster. The cluster was placed among metal-working features in a metallurgical workshop.Scale in cm. Maximum diameter: 8.1 cm. Weight: 75 g. Site Ngre Kataa. 19 July 2008.
Triangular-headed iron projectile point with a barb at the head's base (left) and a long tang (right). To make an arrow (snini in Nafaanra), the tang was inserted into a straight shaft made of bamboo, reed or lightweight wood to which it was hafted. This artifact was found in an area (mound 7) that archaeologists interpret as a house mound. The projectile point shows signs of corrosion by rusting. Scale in cm. Length: 9 cm. Weight: 9.2 g. Site Ngre Kataa. 7 July, 2008.
Iron projectile point with an asymmetrical head (left), a single barbed at the base of the head and a small barb on the opposite side along the tang. To make an arrow, the long tang (right) would have been inserted into a shaft made of bamboo, reed or lightweight wood. This artifact was found in an area (mound 6) that archaeologists interpret as a metallurgical workshop. The point has been corroded by rusting. Scale in cm. Length: 15.2 cm. Weight: 13.7 g. Site Ngre Kataa. 2 June 2009.
Triangular-headed iron projectile point with a single barb at the base of its head (left) and a long thin tang (right). To make an arrow (snini in Nafaanra), the tang was inserted into a shaft made of bamboo, reed or lightweight wood to which it was hafted. The artifact shows signs of corrosion. The point was excavated from a deep midden mound in an disturbed by a pig burrow. Scale in cm. Length: 12.4 cm. Weight: 14.2 g. Site Ngre Kataa. 25 June, 2008.
Triangular-headed projectile point with barbs on either side of the head's base (left). Its long tang (right) is bent. To make an arrow (snini in Nafaanra), the tang was inserted into a straight shaft made of bamboo, reed or lightweight wood to which it was hafted. This artifact was found in an area that archaeologists interpret as a metallurgical workshop. The projectile point shows signs of corrosion by rusting. Scale in cm. Length: 9.8 cm. Weight: 10.2 g. Site Ngre Kataa. 5 July, 2008.
Rights:
Creative Commons Attribution-NonCommercial
Publisher:
University of Victoria Libraries
Provenance:
Ngre Kataa, Mound 6, Unit 44N 6W, Level 3; piece plot: 67-71 cm S, 142-156 W
A piece of a copper alloy (brass) bar, found in association with burned features that archaeologists interpret as linked to metalworking (left: side view; right, end views). The bar is square in cross-section (right). One end appears finished and has a slight circular depression or dimple (bottom right). The other end (top right) is jagged and appears to be broken from a longer bar. The artifact was recovered from soil associated with an amorphous burned feature, underneath which were a series of burned basins likely created by forging activities. The object is similar in appearance to brass bars known from the Ma'adin Ijafen cache of brass ingots documented by Theodore Monod in eastern Mauritania in the 1960s. As such, this may be the form in which metalworkers got the copper alloys that were worked at the site. Length: 1.7 cm. Weight: 2.8 g. Scale in cm. Site Ngre Kataa. 25 June 2009.
A flat, thin iron disk. The object is corroded by rust. Its function is unknown. The disc was found in close association with a large anvil or grinding stone and adjacent to a distinctive pottery vessel and a smaller, irregularly shaped piece of flat iron (SF 09-171). This group of objects was located within an area (mound 6) that archaeologists interpret as a metallurgical workshop. Scale in cm. Width: 9.4 cm. Thickness: .2 cm. Weight: 49.3 g. Site Ngre Kataa. 4 July 2009.
A flat, irregularly shaped iron with circular depression. The object is corroded by rust and its original form and function are unknown. It was found in close association with a large anvil or grinding stone (GS 09-15), a circular iron disk (SF 09-370) and a distinctive pottery vessel (NK 09-787). This group of objects was located within an area (mound 6) that archaeologists interpret as a metallurgical workshop. Scale in cm. Width: 5.7 cm. Thickness: .2 cm. Weight: 9 g. Site Ngre Kataa. 4 July 2009.
Interior view (left) and exterior view (right) of a partial pottery jar. The pot was found insitu near an anvil/grinding stone in an area interpreted by archaeologists as a metallurgical workshop. The jar's everted rim is rounded (right, top). Its exterior surface (right, bottom) shows evidence of layering, with an upper layer of clay added to a leather-hard lower layer before the pot was fired. The pot's walls are thicker than typical domestic pottery. Its find location suggests that it was probably made for an industrial rather than domestic purpose (possible pot bellow?). Dark smudging on the exterior surface affected both the upper and lower layers of clay, implying that it was exposed to high heat in a reducing atmosphere after manufacture. Striations on the vessel's interior (left) are the result of smoothing and forming during manufacture, with a small area of post-manufacture smudging visible (upper left). The vessel's ceramic fabric is tempered with laterite and crushed slag inclusions. It was found in close association with an anvil/grinding stone (GS 09-15), a circular iron disc (SF 09-370) and an irregularly shaped flat piece of iron (SF 09-371). Intact rim's diameter (exterior lip): 13.5 cm. Photo scale in cm. Site Ngre Kataa. 4 July 2009.
Partial iron projectile point, the tip of the head (left) broken off. The base of the head forms a right angle barb with the short tang. The tang (right) would have been inserted into a shaft made of bamboo, reed or lightweight wood to form an arrow. This point was found in an area (mound 7) that archaeologists interpret as a house mound. The artifact is corroded by rust. Scale in cm. Length: 9.1 cm. Weight: 13.6 g. Site Ngre Kataa. 4 June 2009.
Flat, thin iron disk (SF 09-159). The object is corroded by rust and its edges notched in two spots. Its function is unknown. The disc was found in a cluster (cluster D) with an iron bangle (SF 09-158) and two stones whose surfaces showed evidence of grinding. The cluster was part of a wider feature (clusters A-D) that archaeologists interpret as a shrine, which overlaid stratified deposits in a metallurgical workshop (mound 6). Scale in cm. Width: 8.1 cm. Thickness: .2 cm. Weight: 29.8 g. Site Ngre Kataa. 9 June 2009.
A tri-looped iron bangle (SF 09-158). The bangle was formed from a single round iron rod, looped three times at the top (detail, left). The rod is joined with a single twist at the base, with each end of the rod overlaid by a thin iron strap (bottom), causing slight thickening on either side of the twisted base. The bangle was found in close association with a flat iron disc (SF 09-159) and two stones whose surfaces showed evidence of grinding (cluster D). Archaeologists interpret this context as part of a larger shrine feature (clusters A-D) in a metallurgical workshop. The bangle shows signs of corrosion by rusting. Scale in cm. Width: 8.5 cm. Weight: 30.2 g. Ngre Kataa. 9 June 2009.
A large insitu anvil/grinding stone in an area interpreted by archaeologists as a metallurgical workshop. It is associated with several smaller stones that show signs of use as grinding or hammer stones. On the northwest side of the stone is a partial pottery vessel--unusual for its layered construction (NK 09-787). To the right of the partial pot are two flat iron discs (larger, above, SF 09-370 and smaller, below SF 90-371). The smaller grinding stone (upper left of photo) rested, grinding surface down, on top of a pottery jar (NK 09-788) which was exposed in the next excavation level. Photo scale bar in 5 cm increments. Photo arrow pointing north. Site Ngre Kataa. 4 July 2009.
A large insitu anvil/grinding stone in an area interpreted by archaeologists as a metallurgical workshop (two views). It is associated with several smaller stones that show signs of use as grinding or hammer stones. On the northwest side of the large stone (GS 09-15) is a partial pottery vessel--unusual for its layered construction (NK 09-787). Sitting adjacent to the partial pot are two flat iron discs (larger one, above in photo 1, SF 09-370 and smaller, below in photo 1, SF 90-371). A smaller grinding stone (GS 09-24) sits northeast of the anvil stone, positioned with its grinding surface down. It rested on top of a pottery jar (NK 09-788) which was exposed in the next excavation level. An area of fire-hardened sediment to the southeast of the anvil stone (photo 2) is interpreted as part of a forging feature. Photo scale bar in 5 cm increments. Photo arrow pointing north. Site Ngre Kataa. 4 July 2009.
Photo of a globular pottery jar (NK 08-176) found in an area (mound 6) that archaeologists interpret as a metallurgical workshop. The pot was found sitting next to a large grinding stone (GS 08-03). The jar's lip is slightly everted and its upper surface is undecorated. A horizontal band of contiguous diagonal impressions marked in alternating directions ("/\/\") appears above the jar's rounded shoulder. Its lower body and base are darkened and surface treated with fiber roulette impression. Rim diameter: 18cm at exterior lip. Vessel height (base to rim): 17 cm. Photo scale in cm. Site Ngre Kataa. 1 July 2008.
Iron projectile point fragment. The elongated head (left) has a single barb at its base and a short tang (right). The point has been corroded by rusting. Scale in cm. Length: 11.3 cm. Weight: 14 g. Site Ngre Kataa. 26 June 2008.
Photo of a pottery jar with a slightly everted rim (NK 08-406), found insitu in an area that archaeologists interpret as a metallurgical workshop. Above its rounded shoulder, the jar's surface is undecorated, with the possible exception of traces of red pigment in some areas. The jar's shoulder is decorated with a band of circular punctates interspersed with cross-hatched designs, repeated twice around the jar's circumference. Its base and lower body are surface treated with cord roulette in a zone bounded by a band of diagonal impressions which create a zigzag design ("/\/\"). The jar is fire-clouded in zones across its surface. The jar was found in the vicinty of a grinding stone (GS 08-10), a partial tuyere (NK 08-284) and a burned feature. Rim diameter at exterior lip: 20 cm. Vessel height: 19 cm. Site Ngre Kataa. 15 July 2008.
An iron bangle (SF 08-182) made by coiling a flat iron rod with thinned pointed ends. The bangle was found in association with pottery, other bangles and artifacts (cluster A). Archaeologists interpret this context as part of a larger shrine feature (clusters A-D) that capped a metallurgical workshop. The bangle shows signs of corrosion by rusting. Scale in cm. Width: 8.2 cm. Weight: 38.8 cm. Site Ngre Kataa. 15 July 2008.
An iron bangle (SF 08-183) made from a spiral-twisted round iron rod with overlapping ends. The bangle was found in association with pottery, other bangles and a dog cranium and jaws (cluster B). Archaeologists interpret this context as part of a larger shrine feature (clusters A-D) that capped a metallurgical workshop. The bangle shows signs of corrosion by rusting. Scale in cm. Width: 9.5 cm. Weight: 115.5 g. Site Ngre Kataa. 15 July 2008.